SikaMelt®-289
Pressure Sensitive Hot Melt for self-adhesive coating
SikaMelt®-289 is a versatile pressure sensitive hot melt adhesive based on thermoplastic rubber with very good surface tack. Its high tack, soft character and tack stability make SikaMelt®-289 highly suitable for self-adhesive coating of vaious materials. It is combining a good temperature resistance with remarkable self-adhesive properties.
- High tack
- Long term tack stability
- Good temperature resistance
- Wide adhesion range
PRODUCT BENEFITS
- High tack
- Long term tack stability
- Good temperature resistance
- Wide adhesion range
Areas of Application
SikaMelt®-289 is designed for self-adhesive coating of various materials like foils and foams. It is suitable for self-adhering gaskets applied as a foamed bead on PP- or PE-foams for water protection applications specifically used in the Automomotive industry. SikaMelt®-289 is not to be used on substrates containing monomeric plasticizer.This product is suitable for experienced professional users only. Test with actual substrates and conditions have to be performed to ensure adhesion and material compatibility.
Product Details
| Chemical base | Thermoplastic rubber | |
| Color (CQP001-1) | Brownish | |
| Cure mechanism | Physical hardening | |
| Density | 1 kg/l | |
| Viscosity (by Brookfield) | at 190 °C | 8 000 mPa·s |
| Softening temperature (CQP538-5) | 127 °C | |
| Application temperature |
short term max. 1 h | 170 – 190 °C 200 °C A |
| SAFT (CQP560-1) | 96 °C | |
| Peel strength (CQP568-1) | 42 N/25 mm B | |
| Shelf life | 12 months |
| CQP = Corporate Quality Procedure | A) Only valid for nozzle | B) 23 °C 50 % r.h. |
CURE MECHANISM
SikaMelt®-289 is a physically hardening adhesive.
CHEMICAL RESISTANCE
SikaMelt®-289 is resistant to aqueous surfactant, weak acids and caustic solutions.
The chemical resistance is influenced by several factors such as chemical composition, concentration, period of exposure and temperature. Therefore a project related testing in case of chemical or thermal exposure is required.
Application
Surface preparation
Surfaces must be clean, dry and free from grease, oil and dust.
Based on the surface and type of material, a physical or chemical pre-treatment might be required. Type of pre-treatment must be determined by preliminary tests.
Application
With adequate processing equipment SikaMelt®-289 can be applied directly or by transfer method. It can be applied as film, dot, bead or spray application. For automated applications a suitable filter system is required.
Due to the better adhesion performance the direct method is usually chosen whenever possible. The transfer method is often used in combination with substrates that are porous and absorbing such as foams or when they are sensitive to high temperature such as thin PE films. To protect the adhesive surface against dust, light and oxygen it is necessary to cover the adhesive film with silicone coated paper or foil.
To meet the required application properties the adhesive viscosity can be adjusted by adapting the application temperature (see diagram 1).
Diagram 1: Viscosity as function of temperature
During breaks SikaMelt®-289 is to be processed as follows:
For breaks ≥ 1 h the heating needs to be lowered to 80 °C and for breaks ≥ 4 h the heating needs to be switched off.
To guarantee a constant quality during the whole production process it is mandatory to protect the adhesive in the melting tank with nitrogen or carbon dioxide (to avoid possible reaction of the product with oxygen).
For advice on selecting and setting up suitable processing equipment contact the System Engineering Department of Sika Industry.
Removal
SikaMelt®-289 may be removed from tools and equipment with Sika® Remover-208 or another suitable solvent.
Hands and exposed skin have to be washed immediately using hand wipes such as Sika® Cleaner-350H or a suitable industrial hand cleaner and water.
Do not use solvents on skin.
STORAGE CONDITIONS
SikaMelt®-289 has to be stored at temperature below 40 °C in a dry place.
For transportation purposes, the storage temperature can be exceeded for a period of max. 4 weeks up to 60 °C.