SikaBiresin® CR141 CH100-1
SikaBiresin® CR141 CH100-1 is an epoxy resin system suitable for the production of high performance FRP components by RTM process.
- Low viscosity and good wetting characteristics at elevated temperatures
- High temperature resistance
- Short curing cycles
PRODUCT BENEFITS
- Low viscosity and good wetting characteristics at elevated temperatures
- High temperature resistance
- Short curing cycles
Areas of Application
SikaBiresin® CR141 CH100-1 is especially suited to injection processes due to its viscosity and reactivity. It is suited for applications where higher temperature resistance and short cycle times are required.This product is suitable for experienced professional users only. Tests under actual processing conditions and with additional materials such as fibres and release agents must be performed to proof material compatibility.
Packaging
SikaBiresin® CR141 (A)
| Pail | 10 kg |
| Drum | 220 kg |
| IBC | 1000 kg |
SikaBiresin® CH100-1 (B)
| Can | 4 kg |
| Drum | 180 kg |
Product Details
| Properties |
| ||||
| Chemical base |
| ||||
| Color |
| ||||
| Density | liquid cured |
| |||
| Mixing ratio | by weight by volume | 100 : 20 100 : 23 | |||
| Viscosity (CQP029-4) |
mixed |
| |||
| Pot life (CQP021-3 / Gel Timer TECAM) | 80 minutes | ||||
| Curing conditions | 8 hours | 140 °C | |||
| Tensile strength (CQP036-2 / ISO 527) | 69 MPa | ||||
| Tensile modulus (CQP036-2 / ISO 527) | 2350 MPa | ||||
| Tensile elongation (CQP036-2 / ISO 527) | 5.0 % | ||||
| Flexural strength (CQP027-2 / ISO 178) | 120 MPa | ||||
| Flexural modulus (CQP027-2 / ISO 178) | 2700 MPa | ||||
| Compressive strength (CQP028-5 / ISO 604) | 117 MPa | ||||
| Shore D hardness (CQP023-1 / ISO 868) | 85 | ||||
| Impact resistance (CQP038-2 / ISO 179) | 24 kJ/m2 | ||||
| Glass transition temperature (CQP301-5 / ISO 11357) | 148 °C | ||||
| Heat deflection temperature (CQP030-1 / ISO 75A) | 141 °C | ||||
| Heat deflection temperature (CQP030-1 / ISO 75B) | 145 °C | ||||
| Heat deflection temperature (CQP030-1 / ISO 75C) | 122 °C | ||||
| Shelf life |
|
| CQP = Corporate Quality Procedure |
Application
Application
The resin system is optimized for injection temperatures between 45 °C – 80 °C. Consider the change in processing parameters if the resin system is processed at different temperatures. Depending on the process, the mould temperature can be 60 °C – 140 °C for an isothermal process and 60 °C – 180 °C for a variothermal process.
Diagram 1: Viscosity development at different temperatures
Prior to application, check both components for crystallization. The crystallization process can be reversed by heating the product to 60 °C – 70 °C until the crystals are no longer visible.
Containers must be closed tightly immediately after each use to prevent moisture ingress.
Removal
Uncured SikaBiresin® CR141 CH100-1 can be removed from tools and equipment with Sika® Reinigungsmittel 5 or another suitable solvent. Once cured, the material can only be removed mechanically. Hands and exposed skin shall be washed immediately using industrial hand cleaner and water.
Do not use solvents on skin.
STORAGE CONDITIONS
All components must be stored between 15 °C – 30 °C.
Prior to use check the material for homogeneity and crystallization and make sure to temper it to processing temperature.