SikaBiresin® CR120
(formerly Biresin® CR120)
Composite resin system for vacuum infusion process with Tg up to 115 °C
SikaBiresin® CR120 is an epoxy resin system suitable for the production of high performance fiber reinforced composite parts and molds with thermal properties up to 115 °C by vacuum infusion process.
- Fast wetting of dry fabrics and non-wovens
- DNV GL approved with both hardeners. Certificate No. TAK00001YD
- Two hardeners (B) with uniform mixing ratio enable a variation of processing times
PRODUCT BENEFITS
- Fast wetting of dry fabrics and non-wovens
- DNV GL approved with both hardeners. Certificate No. TAK00001YD
- Two hardeners (B) with uniform mixing ratio enable a variation of processing times
Areas of Application
SikaBiresin® CR120 is especially suited to infusion and injection processes due to its low viscosity. It is designed for the production of industrial composite parts as well as molds with an elevated temperature resistance. This product is suitable for experienced professional users only. Tests under actual processing conditions and with additional materials such as fibers and release agents must be performed to proof material compatibility.Packaging
SikaBiresin® CR120 (A)
| Pail | 10 kg |
| Drum | 200 kg |
| IBC | 1000 kg |
SikaBiresin® CH120-3 (B)
| Can | 3 kg |
| Drum | 180 kg |
SikaBiresin® CH120-6 (B)
| Can | 3 kg |
| Hobbock | 20 kg |
Product Details
| Properties |
| ||||
| Chemical base |
| ||||
| Color |
| ||||
| Mixing ratio | by weight by volume |
| |||
| Density | liquid cured |
| |||
| Viscosity (CQP029-4) |
mixed |
| |||
| Pot life (CQP021-3 / Gel Timer TECAM) |
| ||||
| Curing conditions | 12 hours |
| |||
| Tensile strength (CQP036-2 / ISO 527) |
| ||||
| Tensile modulus (CQP036-2 / ISO 527) |
| ||||
| Tensile elongation (CQP036-2 / ISO 527) |
| ||||
| Flexural strength (CQP027-2 / ISO 178) |
| ||||
| Flexural modulus (CQP027-2 / ISO 178) |
| ||||
| Compressive strength (CQP028-5 / ISO 604) |
| ||||
| Shore D hardness (CQP023-1 / ISO 868) |
| ||||
| Impact resistance (CQP038-2 / ISO 179) |
| ||||
| Glass transition temperature by DSC (CQP301-5 / ISO 11357) |
| ||||
| Heat deflection temperature (CQP030-1 / ISO 75B) |
| ||||
| Shelf life |
|
| CQP = Corporate Quality Procedure |
Application
Application
The resin system is optimized for processing temperatures between 18 °C – 25 °C. Consider the change in processing parameters if the resin system is processed at different temperatures. The curing must be performed at temperature ≥ 18 °C.
Information regarding reactivity and viscosity development of different combinations of SikaBiresin® CR120 are shown in the diagrams below.
Diagram 1: Reactivity at 23 °C in a 100 ml insulated cup
Diagram 2: Viscosity development
Prior to application, check both components for crystallization. The crystallization process can be reversed by heating the product to 60 °C – 70 °C until the crystals are no longer visible.
Containers must be closed tightly immediately after each use to prevent moisture ingress.
Removal
Uncured SikaBiresin® CR120 can be removed from tools and equipment with Sika® Reinigungsmittel 5 or another suitable solvent. Once cured, the material can only be removed mechanically. Hands and exposed skin shall be washed immediately using industrial hand cleaner and water.
Do not use solvents on skin.
STORAGE CONDITIONS
All components must be stored between 15 °C – 30 °C.
Prior to use check the material for homogeneity and crystallization and make sure to temper it to processing temperature.