Sikafloor® Marine-100
Lightweight self-leveling primary deck covering mortar for interior decks
Sikafloor® Marine-100 is a 1-component lightweight self-leveling mortar based on polymer modified cement.
Sikafloor® Marine-100 is tested according to FTP Code system and approved according to the IMO Marine Equipment Directives
- Lightweight leveling mortar
- One component, ready to mix
- Easily applicable
- Good leveling properties in thin layers
- Can be pumped
PRODUCT BENEFITS
- Lightweight leveling mortar
- One component, ready to mix
- Easily applicable
- Good leveling properties in thin layers
- Can be pumped
Areas of Application
Sikafloor® Marine-100 is applied on interior decks, to level the surface prior to the application of deck finishing materials such as: carpets, tiles, parquet, rubber and vinyl. It is suitable for application in dry and wet accommodation areas exept for galleys. This product is suitable for experienced professional users only. Test with actual substrates and conditions have to be performed to ensure adhesion and material compatibility.Packaging
Bag | 14 kg |
Product Details
Chemical base | Polymer modified cement mortar | |
Color | Grey | |
Cure mechanism | Hydraulic | |
Density | mixed cured | 1.2 kg/l 0.9 kg/l |
Mixing ratio | per 14 kg bag | 5.9 ─ 6.4 liter |
Substrate temperature | 5 ─ 30 °C | |
Application thickness | max. | 10 mm |
Coverage | per 14 kg bag at layer thickness 1 mm | 15 m2 |
Working time (CQP599-9) | 30 minutes A | |
Ready to walk on (CQP600-3) | depending on humidity and ventilation | 12 hours A |
Compressive strength (CQP599-2) | 7 MPa B | |
Flexural strength (CQP599-1) | 4.2 MPa B | |
Modulus of elasticity in compression (CQP599-6 / EN 13412) | 2 GPa B | |
Linear shrinkage (CQP599-5) | 0.04 % B | |
Shelf life | 12 months C |
CQP = Corporate Quality Procedure | A) 23 °C / 50 % r. h. | B) after 28 days | C) stored in a dry, cool place below 25 °C |
CURE MECHANISM
Sikafloor® Marine-100 cures by way of hydraulic curing.
Application
Surface preparation
For leveling applications, the surface has to be clean, free from dust, grease, oils and other substances, which may impair adhesion. Rust has to be removed with a steel brush or other appropriate means, followed by vacuum cleaning.
The surface has to be primed with Sikafloor® Marine Primer C using a long hair roller. After drying of the Sikafloor® Marine Primer C, Sikafloor® Marine-100 may be applied.
Sikafloor® Marine-100 applications on aluminum or zinc rich shop primer coated decks, require a tie coat of SikaCor® ZP Primer or another suitable tie coat prior the priming step with Sikafloor® Marine Primer C.
Application
Apply the mortar with a steel board or a straight edge. Sikafloor® Marine-100 can also be applied by pinrake.
Sikafloor® Marine-100 has to be applied within 20 minutes after mixing. At temperatures above 30 °C the open time will be reduced to 10 minutes or less.
For advice on selecting and setting up a suitable pump system, contact the System Engineering Department of Sika Industry.
Removal
Excess material can best be removed before curing with a trowel wipe or water.
Fresh Sikafloor® Marine-100 may be removed from tools and equipment with water. Once cured, the material can only be removed mechanically.
Exposed hands and skin shall be washed immediately with water. Use a suitable skin protection hand cream.
Application limits
For applications on slooping surfaces > 1 % contact the Technical Department of Sika Industry.