SikaBiresin® UR595 L4

Elastomeric casting resin for production of parts and molds

No image available

SikaBiresin® UR595 L4 is a 2-component polyurethane elastomeric casting resin for production of parts and molds.  

  • ​​​​​​Good tear strength
  • Casting thickness up to 50 mm
  • Good elongation at break
  • Easy processing
  • Quick setting at room temperature
 
Show all documents
Find this product in your country
Go

Overview

PRODUCT BENEFITS

  • ​​​​​​Good tear strength
  • Casting thickness up to 50 mm

  • Good elongation at break

  • Easy processing

  • Quick setting at room temperature

 

Areas of Application

SikaBiresin® UR595 L4 is designed for production of semi-flexible parts and molds by hand casting or with 2-component low pressure equipment. This product is suitable for experienced professional users only. Tests under actual processing conditions and with additional materials such as coatings and release agents must be performed to proof material compatibility.  

Packaging

  

SikaBiresin® UR505 (A)

Canister

11 kg

Drum225 kg
IBC1125 kg

SikaBiresin® UR595 L4 (B)

Drum

205 kg

 

Product Details

Properties

Component A

SikaBiresin® UR505

Component B

SikaBiresin® UR595 L4

Chemical base

Isocyanate

Polyol

Color

 

mixed

Straw yellow

Orange, light orange

Orange, light orange

Density

 

cured

1.21 kg/l

1.19 kg/l

1.25 kg/l

Mixing ratio

by weight

by volume

55 : 100

54 : 100

Viscosity (CQP029-4)

 

mixed

450 mPa·s

1500 mPa·s

1000 mPa·s

Pot life (CQP021-3 / Gel Timer TECAM)

155 g at 23 °C

4 minutes

Demolding time

at 23 °C

at 80 °C

12 hours

1 hour

Curing time

at 23 °C

5 days

Casting thickness

up to 50 mm

Shore A hardness (CQP023-1 / ISO 868)

94 A

Tensile strength (CQP036-6 / ISO 37)

16 MPa A

Tear strength (CQP045-1 / ISO 34)

64 kN/m A

Elongation at break (CQP 036-6 / ISO 37)

400 % A

BASHORE resilience (ASTM 2632)

25 % A

Glass transition temperature TMA (CQP053-1 / ISO 11359)

0 °C A

Service temperature

-20 – 70 °C

Shelf life

9 months

12 months

CQP = Corporate Quality Procedure

A) curing condition: 80 °C for 12 hours

Application

Surface preparation

The material, processing and mold or master-model temperature shall be between 18 °C – 25 °C.
Make sure the mold or master model is clean, dry, dust and grease free.
If mold or master-model surface is porous, it must be sealed prior applying the release agent.
It is recommended to use wax-based release agents. For further information regarding Sika release agent consult the corresponding Product Data Sheet.

Application

Immediately after mixing pour the Product into the mold starting at the deepest point.
Demolding time may vary depending on casted thickness and room temperature.
To achieve the highest performance, leave the elastomeric mold at a temperature ≥ 23 °C for 5 days before using it.

STORAGE CONDITIONS

Both components must be stored at temperature between 15 °C and 25 °C in original unopened containers.

Documents