SikaBiresin® F150

Unfilled fastcast resin for production of climbing holds

No image available

SikaBiresin® F150 is an unfilled fast curing 2-component polyurethane system with high abrasion resistance for production of climbing holds.  

  • High abrasion resistance
  • High impact resistance
  • Quick setting product
  • Easy processing
  • User friendly mixing ratio
  • Customized colors with SikaBiresin® Colour Paste
 
Show all documents

Overview

PRODUCT BENEFITS

  • High abrasion resistance
  • High impact resistance
  • Quick setting product
  • Easy processing
  • User friendly mixing ratio
  • Customized colors with SikaBiresin® Colour Paste
 

Areas of Application

SikaBiresin® F150 is designed for production of wear resistant and impact resistant climbing holds.
This product is suitable for experienced professional users only.  

Packaging

   

SikaBiresin® F150 (A)

Canister

20 kg

Drum200 kg

SikaBiresin® F150 (B)

Canister

20 kg

Drum225 kg
 

Product Details

Properties

SikaBiresin® F150 (A)

SikaBiresin® F150 (B)

Chemical base

Polyol, unfilled

MDI-based isocyanate, unfilled

Color

 

mixed

Off-white

Yellowish

Off-white

Density

 

cured

1.05 kg/l

1.21 kg/l

1.18 kg/l A

Mixing ratio

by weight

100 : 100

Viscosity (CQP029-4)

 

mixed

450 mPa·s

500 mPa·s

500 mPa·s

Pot life (CQP021-4)

100 g

2 minutes 30 seconds

Demolding time

20 minutes

Shore D hardness (CQP023-1 / ISO 868)

80 A

Tensile strength (CQP036-2 / ISO 527)

40 MPa A

Tensile modulus (CQP036-2 / ISO 527)

1550 MPa A

Elongation at break (CQP036-2 / ISO 527)

50 % A

Flexural strength (CQP027-2 / ISO 178)

65 MPa A

Flexural modulus (CQP027-2 / ISO 178)

1700 MPa A

Impact resistance (CQP038-2 / ISO 179)

70 kJ/m2 A

Abrasion resistance (CQP112-1 / ISO 4649)

375 mm3 A

Glass transition temperature TMA (CQP053-1 / ISO 11359)

75 °C A

Shelf life

12 months

9 months

CQP = Corporate Quality Procedure

A) curing condition: 70 °C for 16 hours

Application

Surface preparation

The material, processing and mold or master-model temperature shall be between 18 °C and 25 °C.
Make sure the mold or master model is clean, dry, dust and grease free.
If mold or master-model surface is porous, it must be sealed prior applying the release agent.
It is recommended to use wax-based release agents. For further information regarding Sika release agent consult the corresponding Product Data Sheet.

Application

Immediately after mixing pour the Product into the mold starting at the deepest point.
Demolding time may vary depending on casted thickness and room temperature.
Further post curing of the demolded part can improve the final mechanical properties.
Depending on the geometry and weight of the part, it is recommended to use a conformer while post curing.
With SikaBiresin® F150 it is recommended using SikaBiresin® SI222 (silicone) for molds.

STORAGE CONDITIONS

Both components must be stored at temperature between 15 °C and 25 °C in original unopened containers.