SikaForce®-641 L3F

Foaming 2-component adhesive for panel bonding

SikaForce®-641 L3F is a fast curing, foaming 2-component polyurethane adhesive for bonding sandwich panels and similar constructions of various materials.  

  • Foaming
  • Low calorific value
  • Black color for acoustic panels
 
Contact
Show all documents

PRODUCT BENEFITS

  • Foaming
  • Low calorific value
  • Black color for acoustic panels
 

Areas of Application

SikaForce®-641 L3F is used for bonding sandwich panels with A2 classification according to EN14509. This product is suitable for experienced professional users only. Tests with actual substrates and conditions have to be performed, ensuring adhesion and material compatibility.  

Product Details

Typical Product Data
Properties

Component A

SikaForce®-641 L3F

Component B

SikaForce®-010

(formerly SikaForce®-7010)

Chemical base

Polyols

Isocyanate derivatives

Color (CQP001-1)

 

mixed

Black

Brown

Black

Cure mechanism

Polyaddition

Density (uncured)

 

mixed (calculated)

1.56 g/cm3

1.23 g/cm3

1.46 g/cm3

Solid content

100 %

100 %

Mixing ratio

by volume

by weight

100 : 45

100 : 35

Viscosity (CQP029-4)

Rheometer, PP25, shear rate 10 s-1, d=1 mm

mixed (calculated)

13 000 mPa∙s A

300 mPa∙s A

9 700 mPa∙s A

Application temperature

15 – 30 °C

Pot-life (CQP536-3)

3 minutes A

Open time (CQP590-3)

8 minutes A

Curing time (CQP590-3)

16 minutes A

Gross calorific potential (EN ISO 1716)

17.2 MJ/kg

Shelf life

6 months

9 months

CQP = Corporate Quality Procedure

A) 23 °C

Technical Information

CURE MECHANISM

The curing of SikaForce®-641 L3F takes place by a chemical reaction of the two components. Higher temperatures speed up the curing process and lower slow it down.

CHEMICAL RESISTANCE

In case of chemical or thermal exposure, conduct project related testing.

Application

Application Information

Surface preparation

Surfaces must be clean, dry and free from grease, oil, dust and contaminants. After the cleaning process, a physical or chemical pre-treatment might be required, depending on surface and type of material. The type of pre-treatment must be determined by tests.
During the curing process, carbon dioxide is released from the adhesive. If none of the substrates are porous, measures need to be taken to allow the carbon dioxide to escape.

Application

Typically a coat weight between 100 and 250 g/m2 is applied, depending on the substrates to be bonded. The coat weight for a given substrate combination must be determined by tests. For A2 classified panels, the maximum coat weight must be determined by calculation according to EN14509.
The product is only suited for use on continuous production lines.
For automated applications, contact the System Engineering Department of Sika Industry.

 

Pressing

An adequate bonding pressure is necessary to obtain a voidless contact between the substrates and the adhesive. The specific pressure is, however, dependent on the core material and must be determined by tests. The pressure must always be below the maximum compressive strength of the core. After starting the press process, do not release the pressure until the press time has elapsed.

Removal

Uncured SikaForce®-641 L3F may be removed from tools and equipment with SikaForce®-096 Cleaner (formerly SikaForce®-7260 Cleaner). Once cured, the material can only be removed mechanically.
Hands and exposed skin have to be washed immediately using hand wipes such as Sika® Cleaner-350H or a suitable industrial hand cleaner and water.

Do not use solvents on skin.

STORAGE CONDITIONS

SikaForce®-641 L3F has to be kept between 10 °C and 30 °C in a dry place. Do not expose it to direct sunlight or frost. After opening of the packaging, the content has to be protected against humidity.
The lowest allowed temperature during transportation is -20 °C for max. 7 days.