SikaBiresin® PX223 HT

Vacuum casting polyurethane for technical parts and prototypes

Image not available

SikaBiresin® PX223 HT is a 2-component vacuum casting polyurethane system for manufacturing of technical parts and prototypes.  

  • High temperature resistance
  • Low viscosity
  • High flexural resistance
  • Good impact resistance
 

Find this product in your country

Go

Overview

PRODUCT BENEFITS

  • High temperature resistance

  • Low viscosity

  • High flexural resistance

  • Good impact resistance

 

Areas of Application

SikaBiresin® PX223 HT is designed for manufacturing of prototype parts and mock-ups by vacuum casting with mechanical properties similar to thermoplastics like filled ABS by casting in silicone molds. This product is suitable for experienced professional users only. Tests under actual processing conditions and with additional materials such as coatings and release agents must be performed to proof material compatibility.  

Packaging

   

SikaBiresin® PX223 HT (A)

Box with tins

6 x 1 kg

Canister5 kg

SikaBiresin® PX223 HT (B)

Box with bottles

6 x 0.8 kg

Canister4 kg
 

Product Details

Properties

SikaBiresin® PX223 HT (A)

SikaBiresin® PX223 HT (B)

Chemical base

Isocyanate

Polyol

Color

 

mixed

Colorless

Black

Black

Density

 

cured

1.17 kg/l

1.12 kg/l

1.14 kg/l

Mixing ratio

by weight

100 : 80

Viscosity (CQP538-2 / BROOKFIELD LVT)

 

mixed

1100 mPa·s

300 mPa·s

850 mPa·s

Pot life (CQP021-3 / Gel Timer TECAM)

90 g at 23 °C

6 minutes

Demolding time

3 mm, at 70 °C

60 minutes

Maximum casting thickness

10 mm

Shore D hardness (CQP023-1 / ISO 868)

23 °C

130 °C

80 A

65 A

Flexural modulus (CQP027-2 / ISO 178)

2300 MPa A

Flexural strength (CQP027-2 / ISO 178)

80 MPa A

Tensile strength (CQP036-2 / ISO 527)

60 MPa A

Elongation at break (CQP036-2 / ISO 527)

11 % A

Impact resistance (CQP038-2 / ISO 179)

60 kJ/m2 A

Linear shrinkage (CQP014-5)

3 x 50 x 250 mm

4 mm/m A

Heat deflection temperature (CQP030-1 / ISO 75A)

110 °C A

Heat deflection temperature (CQP030-1 / ISO 75B)

130 °C A

Glass transition temperature (CQP053-1 / ISO 11359)

120 °C A

Coefficient of thermal expansion (CQP053-1 / ISO 11359)

115 x 10-6 1/K A

Dielectric strength (IEC 60243-1 E2)

50 Hz – 1 mm

27.6 kV/mm A

Dielectric constant (IEC 60250) OUTDATED

ε 100 Hz

3.68 A

Dissipation factor (IEC 60250) OUTDATED

tan δ (100 Hz)

0.012 A

Volume resistivity (IEC 60093 E2)

8.25 x 1015 A

Shelf life

12 months

CQP = Corporate Quality Procedure

A) curing condition: 100 °C for 1 hour + 110 °C for 12 hours

Application

METHOD OF APPLICATION

The material and processing temperature shall be between 18 °C and 25 °C. Temperature of a silicone mold shall be 70 °C.
The material can only be used in a vacuum casting machine.

Application

Immediately after mixing pour the Product into the preheated silicone mold. After casting, place the mold in a preheated oven (70 °C) for 45 ─ 75 minutes, depending on the wall thickness of the parts.
Further post curing of the demolded part can improve the final mechanical properties.
Depending on the geometry and weight of the part, it is recommended to use a conformer while post curing.

STORAGE CONDITIONS

Both components must be stored at temperature between 15 °C and 25 °C in original unopened containers.