SikaBiresin® CR132 FR CH132-7

Flame retardant composite resin system for hand lay-up process with Tg up to 133 °C

SikaBiresin® CR132 FR CH132-7 is a filled epoxy resin system suitable for the production of high performance fibre reinforced composites with flame retardant properties and a Tg up to 133 °C.  

  • Flame retardant: UL94 V-0 classification
  • Very good wetting and non-draining properties
  • High temperature resistance
 
Show all documents

Overview

PRODUCT BENEFITS

  • Flame retardant: UL94 V-0 classification
  • Very good wetting and non-draining properties
  • High temperature resistance
 

Areas of Application

SikaBiresin® CR132 FR CH132-7 is especially suited for the hand lay-up process and can be used in general industrial composite applications which demand higher thermal resistance and flame retardance.
This product is suitable for experienced professional users only. Tests under actual processing conditions and with additional materials such as fibers and release agents must be performed to proof material compatibility.  

Packaging

  

SikaBiresin® CR132 FR (A)

Pail

10 kg

SikaBiresin® CH132-7 (B)

Can

3.2 kg

Drum180 kg
 

Product Details

Properties

Component A

SikaBiresin® CR132 FR

Component B

SikaBiresin® CH132-7

Chemical base

Epoxy resin

Amine hardener

Color

White

Blue

Density

 

cured

1.26 kg/l

0.93 kg/l

1.24 kg/l

Mixing ratio

by weight

by volume

100 : 23

100 : 31

Viscosity (CQP029-4)

 

mixed

5000 mPa·s

30 mPa·s

1900 mPa·s

Application temperature

18 – 25 °C

Pot life (CQP021-3 / Gel Timer TECAM)

200 minutes

Curing conditions

8 hours

125 °C

Tensile strength (CQP036-2 / ISO 527)

42 MPa

Tensile modulus (CQP036-2 / ISO 527)

3500 MPa

Tensile elongation (CQP036-2 / ISO 527)

1.4 %

Flexural strength (CQP027-2 / ISO 178)

67 MPa

Flexural modulus (CQP027-2 / ISO 178)

3800 MPa

Compressive strength (CQP028-5 / ISO 604)

117 MPa

Shore D hardness (CQP023-1 / ISO 868)

88

Impact resistance (CQP038-2 / ISO 179)

12 kJ/m2

Glass transition temperature (CQP301-5 / ISO 11357)

133 °C

Heat deflection temperature (CQP030-1 / ISO 75B)

128 °C

Shelf life

24 months

12 months

CQP = Corporate Quality Procedure

Application

Application

The resin system is optimized for processing temperatures between 18 °C – 25 °C. Consider the change in processing parameters if the resin system is processed at different temperatures. The curing must be performed at temperature ≥ 18 °C.
Prior to application, check both components for crystallization. The crystallization process can be reversed by heating the product to 60 °C – 70 °C until the crystals are no longer visible.
Containers must be closed tightly immediately after each use to prevent moisture ingress.

Removal

Uncured SikaBiresin® CR132 FR CH132-7 can be removed from tools and equipment with Sika® Reinigungsmittel 5 or another suitable solvent. Once cured, the material can only be removed mechanically. Hands and exposed skin shall be washed immediately using industrial hand cleaner and water.
Do not use solvents on skin.

STORAGE CONDITIONS

All components must be stored between 15 °C – 30 °C.
Prior to use check the material for homogeneity and crystallization and make sure to temper it to processing temperature.

Documents